WC-10Co4Cr Carbides foda don injunan gabaɗaya
Bayani
KF-65 babban ingancin WC-10Co4Cr foda ne wanda aka tsara don biyan manyan buƙatun masana'antar man fetur, takarda, da injunan gabaɗaya.Wannan samfurin yana alfahari da girman girman girman 15-45 / 10-38 / 5-30 / 5-15 / 5-25μm, yana sa ya dace da aikace-aikacen da yawa.
KF-65 yana samuwa a cikin nau'i-nau'i daban-daban guda biyu: sinter & crush, da agglomerated & sintered.Ana yin sinter & crush form ta hanyar juyar da foda sannan a niƙa shi cikin ƙananan barbashi, yayin da agglomerated & sintered form ana yin shi ta hanyar ƙara foda zuwa manyan barbashi kafin a juye.Wannan juzu'i yana ba da sauƙi don haɗa KF-65 a cikin tsarin masana'antar ku kuma cimma sakamakon da ake so.
Bugu da ƙari kuma, KF-65 yana kwatankwacin sauran manyan samfuran kamar AMPERIT 554/556/557/558, METCO/AMDRY 5843/5163, WOKA 3903/3615/3652/3655/3665, PRAXAIR WC-113 /WC-7311350, da PAC 1500. Wannan yana tabbatar da cewa kun karɓi samfurin mafi kyawun inganci wanda ya dace da ma'auni iri ɗaya kamar sauran samfuran manyan masana'antu.
Ɗaya daga cikin manyan fa'idodin KF-65 shine ikonsa na yin aiki azaman madadin plating na chromium mai wuya.Wannan muhimmin la'akari ne ga kamfanonin da ke neman rage tasirin muhalli da kuma bi ka'idoji.Bugu da ƙari, KF-65 na iya samar da ƙarewar ƙasa mai laushi, ragewa ko ma kawar da buƙatar bayan-machining.Wannan zai iya adana lokaci da kuɗi a cikin tsarin masana'antu, yayin da yake ba da sakamako mai kyau.
Ko kuna neman haɓaka aikin kayan aikin ku, rage tasirin muhallinku, ko haɓaka ingancin samfuran ku kawai, KF-65 kyakkyawan zaɓi ne.Amintaccen bayani ne mai inganci kuma mai tsada wanda zai iya biyan buƙatun masana'antu iri-iri, gami da man fetur, takarda, da injunan gabaɗaya.Gwada shi a yau kuma ku fuskanci bambanci da kanku.
Makamantan samfuran
Alamar | Sunan samfur | AMPERIT | METCO/AMDRY | WOKA | PRAXAIR | PAC |
KF-65 | Saukewa: WC-10Co4Cr | 554 | 5843 | 3903 | Saukewa: WC-113WC-436-1 | |
Saukewa: WC-10Co4Cr | 556/557/558 | 5163 | 3651/36523655/3665 | Saukewa: WC-7311350 | 1500 | |
Saukewa: WC-10Co4Cr | . | . | 3660FC | . | 1500 |
Ƙayyadaddun bayanai
Alamar | Sunan samfur | Girman Barbashi (μm) | Chemistry (wt%) | Nau'in | Yawaita bayyananne | Yawowa | Kayayyaki | Aikace-aikace | |||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Co | C | Fe | W | Cr | B | Si | Ni | ||||||||
KF-65 | Saukewa: WC-10Co4Cr | 15-45, 10-38 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Sinter&Crush | 5.5-6.5g/cm3 | ≤25s/50g | APS, HVOF, HVAF | Madadin wuya chromium plating;Man fetur, takarda, kayan aikin gabaɗaya | |||
KF-65 | Saukewa: WC-10Co4Cr | 15-45,10-38,5-30 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated da sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS, HVOF, HVAF | Madadin wuya chromium plating;Man fetur, takarda, kayan aikin gabaɗaya | |||
KF-65 | Saukewa: WC-10Co4Cr | 5-25, 5-15 | 9.5-10 | 5.3-5.6 | ≤0.8 | Bal. | 3.5-4.0 | Agglomerated da sintered | 3.5-4.8 g/cm3 | Tsayayyen ciyarwa zuwa foda feeder | HVOF, HVAF | Alternative hard chromium plating;Smoother surface, less ko free post machining; | |||
KF-60 | WC-12C | 15-45, 10-63 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Sinter&Crush | 5.5-6.5 g/cm3 | ≤25s/50g | APS, HVOF | Wear juriya, Fretting lalacewa juriya | ||||
KF-60 | WC-12C | 15-45, 10-38, 5-30 | 10.5-12 | 4.9-5.4 | ≤0.8 | Bal. | Agglomerated da sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS, HVOF, HVAF | Wear juriya, Fretting lalacewa juriya; janar injuna | ||||
KF-61 | WC-17C | 15-45, 10-38 | 15.5-17 | 4.5-5.1 | ≤0.8 | Bal. | Agglomerated da sintered | 3.5-5.5 g/cm3 | ≤25s/50g | APS, HVOF, HVAF | Wear juriya, Fretting sa juriya, Mafi tauri; janar kayan | ||||
KF-62 | WC-25C | 15-45, 10-38 | 22-26 | 4.0-4.6 | ≤0.8 | Bal. | Agglomerated da sintered, Densification | 3.0-5.5 g/cm3 | ≤25s/50g | APS, bindigogi masu fashewa, feshin sanyi | Fretting lalacewa juriya, Mafi tauri | ||||
KF-66 | WC-23% CrC-7Ni | 15-45, 10-38 | 6.0-6.8 | ≤0.8 | Bal. | 16.5-20 | 5.5-7 | Agglomerated da sintered | 3.0-5.0 g/cm3 | ≤25s/50g | APS, HVOF, HVAF | Alternative hard chromium plating;An yi amfani da shi don ƙarancin maida hankali acid/alkali yanayi a 200 ℃;Anti oxidation da sa juriya a 750 ℃ | |||
KF-66 | 43WC-43% CrC-14Ni | 15-45,10-38 | 7.8-8.4 | ≤0.8 | Bal. | 35-38 | 12-14 | Agglomerated da sintered | 2.0-4.0 g/cm3 | ≤35s/50g | APS, HVOF, HVAF | Alternative hard chromium plating Ana amfani dashi don ƙarancin maida hankali acid/alkali yanayi a 200 ℃ | |||
KF-63 | WC-10 Ni | 15-45,10-38 | 4.5-5.2 | ≤0.1 | Bal. | 8.5-10.5 | Agglomerated da sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | APS, HVF, HVAF | Non Magnetic lalacewa juriya shafi.Kyakkyawan juriya na lalata | ||||
KF-70 | Cr3C2-25NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 18-21.5 | Agglomerated da sintered | ≥2.3 g/cm3 | Tsayayyen ciyarwa zuwa foda feeder | APS, HVOF | Anti oxidation da sa juriya a 815 ℃ | ||||
KF-69 | Saukewa: Cr3C2-20NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated da sintered | ≥2.3 g/cm3 | Tsayayyen ciyarwa zuwa foda feeder | APS, HVOF | Anti oxidation da sa juriya a 815 ℃ | ||||
KF-71 | Saukewa: Cr3C2-30NiCr | 15-45, 20-53 | 9-11 | ≤1 | Bal. | 15-17.5 | Agglomerated da sintered | ≥2.3 g/cm3 | Tsayayyen ciyarwa zuwa foda feeder | APS, HVOF | Anti oxidation da sa juriya a 815 ℃.Gara tauri | ||||
KF-60 | WC-12Co (Ƙarancin Carbon) | 15-45, 20-53 | 10.5-12 | 4.0-4.4 | ≤0.8 | Bal. | Agglomerated da sintered | 4.0-6.0 g/cm3 | ≤18 s/50g | HVOF, HVAF | An yi amfani da shi don jujjuyawar wanka na Zn a cikin Layin Galvanizing Ci gaba | ||||
KF-68 | Saukewa: WC-30WB-10C | 15-45,20-53,10-38 | 9-11 | 3.5-3.9 | Bal. | 1.4-1.7 | Agglomerated da sintered | 3.0-4.9 g/cm3 | ≤30s/50g | HVOF, HVAF | An yi amfani da shi don jujjuyawar wanka na Zn a cikin Layin Galvanizing Ci gaba | ||||
KF-68 | Saukewa: WC-30WB-5Co5Cr | 15-45,20-53,10-38 | 4-6 | 3.5-3.9 | Bal. | 4-6 | 1.4-1.7 | Agglomerated da sintered | 3.0-4.9 g/cm3 | ≤30s/50g | HVOF, HVAF | An yi amfani da shi don jujjuyawar wanka na Zn a cikin Layin Galvanizing Ci gaba | |||
KF-300E | 35% WC-NiCrBSi | 15-53,45-104 | 2.5-3.2 | 1.0-2.6 | 32-35 | 7.5-9 | 1.5-1.9 | 2.0-2.7 | Bal. | WC da NiCrBSi suna samar da gami | 4.0-4.9 g/cm3 | ≤16 s/50g | HVOF, PS | Alternative Blended type WC + Ni60;Mafi yawan amfani da kayan aiki, rage yawan amfani da makamashi, ƙananan tasirin zafi;Amfani da gilashin gilashi | |
KF-300F | 50% WC-NiCrBSi | 15-53,45-104 | 3.2-4.3 | 0.8-2.0 | 45-48 | 5.8-7.2 | 1.0-1.7 | 1.5-2.4 | Bal. | WC da NiCrBSi suna samar da gami | 5.0-7 g/cm 3 | ≤16 s/50g | HVOF, PS | Alternative Blended type WC + Ni60;Mafi yawan amfani da kayan aiki, rage yawan amfani da makamashi, ƙananan tasirin zafi;Amfani da gilashin gilashi |